| Product |
Type |
Solvent and Co-solvent |
Type of emulsifier |
MFFT, ºC |
Solid Content, % |
Brookfield viscosity 25 ºC CPs |
pH |
Applications |
| Accuacril 2011 |
W/B Self-crosslinking modified acrylic copolymer dispersion |
|
Surfactant free |
< 7 |
43-45 |
100-700 |
8 - 9 |
Wood varnishes, Wood stain, Paints and varnishes for exterior wood doors and windows
Industrial applications for wood doors and windows (robot, airless, flow coating)
Water paints for plastic supports |
| Accuacril 2035 |
W/B Self-crosslinking modified acrylic copolymer dispersion |
|
Surfactant free |
< 20 |
39-41 |
40-200 |
8 - 9 |
Wood sealers. Furniture varnishes with blocking resistance.Industrial wood varnishes.Matt coatings for furniture. |
| Accuacril 2037 |
W/B Self-crosslinking modified acrylic copolymer dispersion |
|
Surfactant free |
< 25 |
40-42 |
40-200 |
7 - 8,5 |
Wood sealers
Furniture varnishes with blocking resistance.Industrial wood varnishes
Matt coatings for furniture
Quick drying and sandability for wood primers |
| Accuacril 2123 |
Aqueous hydroxy acrylic resin to combine with water polyisocyanates |
Naphta 100 (1,8%) / Butylglycol (1,8%) |
|
|
40,5 – 43,5 |
300 - 3.300 |
7,0 – 8,3 |
To formulate 2-pack topcoats. OH content: 4 %. Neutralization agent: DMEA
Recommended in refinishing, industrial and plastic coats formulations
Because its good mechanical and thermodynamic stability is possible made pigmented coats |
| Accuacril 2129 |
Aqueous hydroxy acrylic resin to combine with water polyisocyanates |
Solvent Naphta 100 (4%) / Butylglycol (4%) |
|
|
42 - 46 |
300 - 1.500 |
7,5-8,5 |
Two-component clear and topcoats for vehicle repair applications and industrial applications. Combined with aliphatic polyisocyanates in aqueous formulations. OH content: 3,3 %. Neutralization agent: DMEA
One-component industrial baking coatings
• Combined with melamine resins
• Combined with blocked polyisocyanates for waterborne |
| Synthemul 5610 |
W/B Acrylic dispersion |
|
Anionic |
-5 |
49 - 51 |
< 200 |
3,2-4,3 |
As binder in pigmented printing
As coating to back of carpets, high pile, with a good dimensional stability
As adhesive in textile flocking, it can be mechanically foaming |
| Synthemul 5682 ECO |
W/B Acrylic dispersion |
|
Non ionic |
< 0 |
54 – 56 |
< 1000 |
6,7-7,9 |
As an adhesive for textile flocking applications (can be foamed)
As an adhesive for textile laminates (chemical spun bond for non-woven applications)
For coating textiles
As a textile printing binder
Adhesion in a wide range of substrates |
| Synthemul 5686 ECO |
W/B Acrylic dispersion |
|
Non ionic |
< 0 |
54 - 56 |
100 – 1.000 |
6,5 – 7,9 |
As an adhesive for textile flocking applications (can be foamed)
As an adhesive for textile laminates (chemical spun bond for non-woven applications)
For coating textiles
As a textile printing binder. |
| Synthemul 6600 |
W/B Acrylic dispersion |
|
Anionic |
- |
21 |
< 100 |
8 - 9 |
Impregnation
Improve adhering on leather whit faulty penetration
No tacky |
| Synthemul 7611 |
W/B Acrylic dispersion |
|
Anionic |
- |
30-31 |
20 - 50 |
2,5 – 3,5 |
Thickener for water paints. It has also an effect as anti-settling agent for pigment and extenders in the formulation
Thickener agent in any textile application |